Swash plate and production method of the same

ABSTRACT

A swash plate  3  includes an substrate  11  made of an iron-based material, a hard first resin layer  12  provided to coat an end surface of the substrate  11,  and a soft second resin layer  13  provided to coat the first resin layer  12.  A spiral annular groove  12 A is formed in a surface of the first resin layer  12,  and the second resin layer  13  is provided to match a sectional shape of the first resin layer  12.  With the soft second resin layer  13  on a sliding surface  3 A of the swash plate  3,  the swash plate  3  having a good fit in an initial stage of sliding can be provided. When the second resin layer  13  partially wears, a protrusion  12  of the first resin layer  12  of hard resin is exposed, and thus the swash plate  3  having good wear resistance can be provided. The swash plate  3  having good sliding properties can be provided.

Technical Field

The present invention relates to a swash plate and a production method thereof, and more particularly to a swash plate for a swash plate type compressor mounted in an automobile and a production method thereof.

BACKGROUND ART

A conventionally known swash plate type compressor includes a swash plate rotated by a rotating shaft, a plurality of shoes that slide with respect to the swash plate, and a plurality of pistons that slide with respect to the plurality of shoes and reciprocate (for example, Patent document 1).

For such a conventional swash plate type compressor, to improve sliding properties between the shoe and the swash plate, it has been proposed that, for example, an end of the shoe is formed to have a convex shape with a high middle side or a sliding surface of the swash plate is improved (Patent documents 2 and 3). Also, to improve sliding properties, proposals have been made on an improvement in a sliding surface of a bearing as a sliding member or in material (for example, Patent documents 4 to 6).

PRIOR ART DOCUMENTS Patent Documents

Patent document 1: Japanese Patent Laid-Open No. 2008-185124

Patent document 2: National Re-publication of International Patent Application No. WO2002-075172

Patent document 3: Japanese Patent Laid-Open No. 9-71899

Patent document 4: Japanese Patent Laid-Open No. 7-259863

Patent document 5: Japanese Patent Laid-Open No. 2002-39186

Patent document 6: Japanese Patent Laid-Open No. 2007-204602

SUMMARY OF INVENTION Technical Problem

Clutchless swash plate type compressors have been recently widely used. In such a clutchless swash plate type compressor, a swash plate is always rotated in an operation state of an engine of an automobile. In this case, a variable capacity swash plate type compressor is a precondition, and when a car air conditioner is not used, the swash plate is maintained perpendicularly to a rotating shaft. In this state, a piston of the swash plate type compressor does not reciprocate, and thus a coolant and mist-like lubricating oil are not circulated in a cylinder of the swash plate compressor. Specifically, since the coolant and the mist-like lubricating oil are not circulated in the swash plate type compressor, an insufficient amount of lubricating oil is supplied to a sliding portion between the swash plate and the shoe to cause poor lubrication. Further, the coolant itself washes the lubricating oil, and the sliding portion between the swash plate and the shoe easily falls under a boundary lubrication condition to a dry sliding condition. Thus, the clutchless swash plate type compressor has disadvantages that frictional heat in sliding between the shoe and the swash plate increases wear of a resin layer that forms a sliding surface of the swash plate, or seizure of the resin layer of the swash plate occurs.

Also, for a swash plate with a sliding surface coated with a resin layer, wear of the resin layer causes a plated layer or a metal layer as an intermediate layer to be exposed and easily causes seizure.

It may be conceivable to use, as a swash plate, a sliding member disclosed in Patent Literature 4, that is, a sliding member including a metal material placed on a surface of a substrate and having an annular groove in a surface. However, the sliding member in Patent document 4 is supposed as a plain bearing of a crankshaft, and for the plain bearing, sufficient lubricating oil is forcedly supplied to a sliding surface. Thus, the sliding member in Patent Literature 4 can obtain sufficient sliding properties as the plain bearing. However, if the sliding member in Patent Literature 4 is used as a swash plate in the poor lubrication state as described above, the metal swash plate comes into contact with the metal shoe to easily cause seizure on the sliding surface.

Solution to Problem

In view of the above-described circumstances, the present invention according to claim 1 provide a swash plate having a sliding surface that slides with respect to a shoe, including: a substrate made of any of iron-, aluminum-, or copper-based materials; a hard first resin layer provided to coat a surface of the substrate and having an annular groove formed in an outer side surface; and a soft second resin layer provided to coat the surface of the first resin layer and formed to match a sectional shape of the annular groove in the first resin layer, wherein in an initial stage of sliding with respect to the shoe, the second resin layer is the sliding surface, and when the second resin layer partially wears and a protrusion of the annular groove in the first resin layer is exposed, the protrusion and the second resin layer adjacent to the protrusion are the sliding surface.

The present invention according to claim 5 provides a production method of a swash plate according to any of claims 1 to 5, including the steps of: applying a resin paint for a first resin layer composed of hard resin to an end surface of a substrate to provide the first resin layer; drying and/or baking the first resin layer and then forming a minute annular groove in a surface of the first resin layer; applying a resin paint for a second resin layer composed of soft resin to the first resin layer provided with the annular groove; then rotating the substrate at high speeds to remove unnecessary parts of the resin paint for the second resin layer; and forming the second resin layer to match a sectional shape of the surface of the first resin layer.

Effects of Invention

According to the above-described configuration, the soft second resin layer is the sliding surface in the initial stage of sliding, thereby providing a swash plate having a good fit to the shoe. After sliding with respect to the shoe, the hard first resin layer is exposed as the sliding surface and slides with respect to the shoe, thereby providing a swash plate having good wear resistance.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a sectional view of essential portions of an embodiment of the present invention.

FIG. 2 is an enlarged sectional view of essential portions of a swash plate 3 shown in FIG. 1.

FIG. 3 is a sectional view of the portion shown in FIG. 2 partially wearing and a perspective view of a surface shown together.

FIG. 4 shows a difference in sliding properties between the embodiment of the present invention and comparative members.

DESCRIPTION OF EMBODIMENTS

Now, the present invention will be described based on a shown embodiment. In FIG. 1, reference numeral 1 denotes a sliding device provided in a housing of a variable capacity swash plate type compressor. The sliding device 1 includes a swash plate 3 mounted to a rotating shaft 2 journaled in the housing, and a plurality of shoes 4 that slide with respect to the swash plate 3.

The swash plate 3 is formed into a disk shape, and opposite end surfaces of the swash plate 3 are sliding surfaces 3A and 3B that slide with respect to the shoes 4. The swash plate 3 is adjusted in inclination angle with respect to the rotating shaft 2 by unshown inclination angle adjustment means. Meanwhile, the shoe 4 is generally made of semi-spherical metal, and has a flat sliding surface 4A that slides with respect to the sliding surface 3A or 3B of the swash plate 3 and a semi-spherical surface 4B.

In the housing of the swash plate type compressor, a plurality of pistons 5 are provided in parallel with and to surround the rotating shaft 2. A pair of shoes 4 are slidably held in a notch 5A formed in one end of each piston 5, the notch 5A in that state is placed to cover an outer peripheral portion of the swash plate 3, and sliding surfaces 4A of each pair of shoes 4 are abutted against the sliding surfaces 3A and 3B of the swash plate 3. The other end of each piston 5 is slidably fitted in an unshown cylinder provided in the housing.

When the rotating shaft 2 is rotated, the swash plate 3 is rotated, and the sliding surfaces 3A and 3B that are opposite end surfaces of the swash plate 3 slide with respect to the sliding surfaces 4A of each pair of shoes 4, which moves each piston 5 forward and backward in the cylinder via each pair of shoes 4. The above-described configuration is the same as that of a conventionally known sliding device.

Thus, in this embodiment, the sliding surfaces 3A and 3B that are opposite end surfaces of the swash plate 3 are improved as described below to improve sliding properties of the swash plate 3.

Specifically, as shown in a sectional view of essential portions in FIG. 2, the swash plate 3 of this embodiment has a disk-shaped iron-based substrate 11, and a first resin layer 12 of hard resin is provided to coat the entire surface of one end surface 11A of the substrate 11.

In this embodiment, as a material for the first resin layer 12, a material is used composed of a thermosetting resin binder to which at least one of graphite, carbon, MoS₂ and PTFE is added. Adding a hard material such as alumina besides any of the above-described additives can further increase strength of the first resin layer 12.

The thermosetting resin binder includes, for example, polyimide resin (PI), polyamide-imide resin (PAI), epoxy resin, phenol resin, polyamide (nylon), and elastomer. Specifically, a thermosetting resin binder such as a vanish of aromatic polyimide, polyether imide, polyester imide or aromatic polyamide-imide, or diisocyanate-, BPDA-, sulfone-modified resin thereof are preferably used.

The graphite and carbon preferably have high crystallinity. Particularly, a preferable spacing is 3.5 angstroms or less, which reduces variations in friction coefficient in sliding. The graphite and carbon may be natural or artificial ones, but the artificial graphite and carbon are preferable in terms of wear resistance, and the natural graphite and carbon are preferable in terms of seizure resistance and low friction. An average particle diameter of the graphite and carbon is not particularly limited, but graphite and carbon having an average particle diameter of 10 μm or more are used to further improve wear resistance when a load is applied. Meanwhile, graphite and carbon having an average particle diameter of less than 10 μm are preferably used to finely disperse the graphite and carbon in the thermosetting resin binder to provide good wear properties of the binder and further reduce variations in friction coefficient. Thus, the graphite and carbon having the average particle diameter of 10 μm or more and the graphite and carbon having the average particle diameter of less than 10 μm are preferably used at an appropriate ratio in combination.

Particularly preferable PTFE is granular baked PTFE. The baked PTFE is prepared by heating (baking) PTFE powder obtained by suspension polymerization or emulsion polymerization to a melting temperature and then grinding the powder, or prepared by compressing and shaping the powder before baking and grinding the powder after the baking. Particularly preferable PTFE is obtained by once shaping powder obtained by suspension polymerization and then baking and grinding the powder. Such baked powder can be used to obtain relatively hard PTFE, good low friction properties, and also good wear resistance.

The baked PTFE is granular, and an average particle diameter thereof is not particularly limited, but PTFE having an average particle diameter of 7 μm or more is used to achieve better low friction properties and also better wear resistance. Meanwhile, PTFE having an average particle diameter of less than 7 μm is preferably used to finely disperse the PTFE in the thermosetting resin binder to provide good friction properties of the thermosetting resin binder. Thus, the PTFE having the average particle diameter of 7 μm or more and the PTFE having the average particle diameter of less than 7 μm are preferably used at an appropriate ratio in combination.

The first resin layer 12 preferably has a component composition of 10% to 50% by mass of graphite, the balance being the thermosetting resin binder, and MoS₂ or PTFE may be added as required within a range of 1% to 30% by mass. An amount of PTFE is smaller than that of MoS₂, and a total amount of PTFE and MoS₂ is smaller than that of graphite.

A spiral annular groove 12A is formed across the enter surface of the first resin layer 12 in a circumferential direction at radially regular pitches. A height of a protrusion 12B of the annular groove 12A, that is, a depth of a recess 12C of the annular groove 12A is the same across the entire surface of the first resin layer 12.

Further, a second resin layer 13 is provided to coat the entire surface of the first resin layer 12 formed with the annular groove 12A. As a material for the second resin layer 13 of soft resin, a thermosetting resin binder is used to which at least one of low friction materials such as MoS₂ or PTFE is added.

The second resin layer 13 has a component composition of 30% to 80% by mass of MoS₂, the balance being the thermosetting resin binder, and PTFE may be added as required within a range of 1% to 30% by mass. An amount of PTFE added is smaller than that of MoS₂.

Since the second resin layer 13 is provided to match a sectional shape of the surface of the first resin layer 12, a spiral annular groove 14 matching the surface shape of the first resin layer 12 is maintained in a surface that forms the sliding surface 3A. The swash plate 3 is produced via a production process described later, and thus extremely minute countless irregularities are formed in the entire surface of the second resin layer 13. This can improve holding properties of lubricating oil in the surface of the second resin layer 13, that is, the sliding surface 3A.

A thickness t1 of the first resin layer 12 is about several to 30 times larger than a thickness t2 of the second resin layer. The thicknesses t1 and t2 herein refer to thicknesses at a position of a top of the protrusion 12B.

A thickness A of a portion of the second resin layer 13 at the recess 12C is slightly larger than a thickness B of a portion of the second resin layer 13 at the top of the protrusion 12B. More specifically, the size relationship thereof is 3/2A≧B.

Based on the thickness relationship of the resin layers 12 and 13 described above, in this embodiment, the thickness of the first resin layer 12 is set to 3 to 70 μm, while the thickness of the second resin layer 13 is set to 1 to 40 μm. More preferably, the thickness of the first resin layer 12 is 5 to 50 μm and the thickness of the second resin layer 13 is 3 to 10 μm.

In this embodiment, one sliding surface 3A of the swash plate 3 is formed as described above, and the other sliding surface 3B not shown in FIG. 2 is also formed in the same manner as the sliding surface 3A.

As described above, in the swash plate 3 of this embodiment, the surface of the substrate 11 is coated with the first resin layer 12, the annular groove 12A is formed across the entire surface of the first resin layer 12, and the surface of the first resin layer 12 is further coated with the second resin layer 13. Specifically, an intermediate layer conventionally provided between the substrate 11 and the resin layer is omitted in this embodiment.

Next, a production process of the swash plate 3 of this embodiment will be described. Specifically, in this embodiment, the disk-shaped substrate 11 made of an iron-based material is first prepared. Then, a thermosetting resin binder and at least one of graphite, carbon, MoS₂ and PTFE are mixed with a proper amount of organic solvent to prepare a resin paint for the first resin layer 12. The organic solvent adjusts viscosity and facilitates mixing, and any organic solvents may be used without limitation as long as it can dissolve a thermosetting resin binder. For example, when the thermosetting resin binder is polyamide-imide, xylene, N-methyl-2-pyrolidone, toluene, or the like may be used.

Then, the resin paint for the first resin layer is applied to flat opposite end surfaces of the substrate 11, and dried or/baked. As a painting method, for example, spray painting, roll painting, electrostatic painting or stamping painting may be used. Thus, the first resin layer 12 is formed to coat the opposite end surfaces of the substrate 11. Adding a hard material such as alumina besides the above-described additives can further increase strength of the first resin layer 12.

Next, after the resin layer 12 on the opposite end surfaces is dried and/or baked, the annular groove 12A is formed across the enter surface of the first resin layer 12 in a circumferential direction at radially regular pitches. The annular groove 12A may be formed by cutting with a lathe or transferring a groove shape with a press or a roller.

Further, a resin paint for the second resin layer 13 separately prepared is applied to coat the entire surface of the first resin layer 12 formed with the annular groove 12A. The resin painting for the second resin layer 13 is a mixture of a thermosetting resin binder and at least one of low friction materials such as MoS₂ or PTFE with a proper amount of organic solvent, and is applied to the entire surface of the first resin layer 12 formed with the annular groove 12A. Then, a through hole at the center of the substrate 11 is fitted on a drive shaft to rotate the substrate 11 at high speeds for a desired time. Thus, an excess of the resin paint for the second resin layer applied to the surface of the first resin layer 12 is thrown off by a centrifugal force and removed.

Then, the resin paint is again dried and/or baked. Thus, the second resin layer 13 in this embodiment is provided to have the above-described thickness so as to match the sectional shape of the surface of the first resin layer 12, and the above-described minute countless irregularities are formed in the entire surface of the second resin layer 13. As such, the swash plate 3 of this embodiment is produced.

The minute countless irregularities may be formed in the entire surface of the second resin layer 13 of the swash plate 3 of this embodiment for the following reasons. Specifically, in this embodiment, the mixture of the thermosetting resin binder to which MoS₂ or the like is added with the organic solvent is used as the resin paint for the second resin layer 13. Specifically, the resin paint for the second resin layer 13 in which countless particles of MoS₂ are evenly mixed in the liquid thermosetting resin binder is applied to the surface of the first resin layer 12. Then, when the substrate 11 is rotated, from the resin paint for the second resin layer 13, the thermosetting resin binder located on the side closest to the surface is thrown off by the centrifugal force, and also the surface side of the thermosetting resin binder coating each particle of MoS₂ is thrown off. Thus, the countless particles of MoS₂ mixed in the thermosetting resin binder are exposed on the surface, and the thermosetting resin binder is dried and baked in that state. Thus, it is supposed that the countless particles of MoS₂ are exposed on the surface of the cured thermosetting resin binder, and thus the countless minute irregularities are formed across the entire surface of the second resin layer 13 in the embodiment.

The second resin layer 13 may be formed by the following method. Specifically, with the substrate 11 being rotated, the resin paint for the second resin layer is applied to the central side of the first resin layer 12 on the substrate 11. In this case, the substrate 11 is being rotated, and thus the paint applied to the central side of the opposite end surfaces of the substrate 11 is moved radially outwardly by the centrifugal force, and an unnecessary resin paint for the second resin layer is thrown off and removed. Thus, as the above-described embodiment, the second resin layer 13 can be formed to match the sectional shape of the surface of the first resin layer 12 across the entire surface.

Then, immediately after the finish of the production, as shown in FIG. 2, the entire surface of the sliding surface 3A (3B) of the swash plate 3 of this embodiment is coated with the second resin layer 13. Specifically, in the swash plate 3 of this embodiment, the resin layer 12 is not exposed to the surfaces of the sliding surfaces 3A and 3B in the state before sliding with respect to the shoes 4 (the state in FIG. 2). Thus, in an initial stage of sliding with respect to the shoe 4, the second resin layer 13 is the sliding surface 3A (3B) that slides with respect to the sliding surface 4A of the shoe 4.

On the other hand, when time passes after the swash plate 3 is mounted to the rotating shaft 2 and then the sliding surfaces 3A and 3B slide with respect to the sliding surface 4A of the shoe 4, the second resin layer 13 coating the protrusion 12A and the top of the protrusion 12A wear (see FIG. 3). In this state, the top of the protrusion 12A of the first resin layer 12 and the second resin layer 13 adjacent thereto form the sliding surface 3A (3B) and slide with respect to the sliding surface 4A of the shoe 4.

According to the swash plate 3 of this embodiment, in the initial stage of sliding in which the sliding surfaces 3A and 3B start sliding with respect to the sliding surface 4A of the shoe 4, the second resin layer 13 of soft resin coating the top of the protrusion 12B wears to provide a good fit of the sliding surfaces 3A and 3B of the swash plate 3.

Then, as shown in FIG. 3, when the protrusion 12B of the first resin layer 12 and the second resin layer 13 adjacent thereto in the swash plate 3 wear due to sliding with respect to the shoe 4 and the protrusion 12B is exposed, the protrusion 12B and the remaining portion of the second resin layer 13 adjacent thereto as the sliding surfaces 3A and 3B slide with respect to the sliding surface 4A of the shoe 4.

In this state, the protrusion 12B of the first resin layer 12 of hard resin supports the shoe 4, and in this state, the second resin layer 13 of soft resin also slides with respect to the sliding surface 4A of the shoe 4. Then, in this state, the lubricating oil is held in the countless minute irregularities in the surface of the second resin layer 13. This can maintain good seizure resistance and wear resistance of the sliding surfaces 3A and 3B in this embodiment.

FIG. 4 compares sliding properties between the swash plate 3 of this embodiment configured as described above and swash plates 3 of comparative members 1 to 4 with surfaces of substrates 11 being coated with different coating layers. More specifically, sliding properties on wear resistance, seizure resistance, oil holding properties and low friction are compared between this embodiment and the comparative members 1 to 4 under the condition of very poor lubrication.

In FIG. 4, POOR refers to no effect, FAIR refers to poor effect, GOOD refers to good, VERY GOOD refers to very good. The test conditions were as described below.

Testing machine: High pressure atmosphere testing machine

RPM: 9500 rpm

Load: 16 MPa maximum

Type of oil: Mixture of refrigerating machine oil and coolant

Lubrication: Lubricant spraying

Counterpart shaft: SUJ2

As shown in FIG. 4, it is apparent that the swash plate 3 of this embodiment has good wear resistance, very good seizure resistance and oil holding properties, and low frictional resistance.

Unlike this embodiment, in the comparative member 1, the surface of the substrate 11 is coated with a flat metal coating (Cu alloy spray layer) with an even thickness. For the comparative member 1, there were poor effect of oil holding properties and no effect of other sliding properties. Particularly, evaluation of wear resistance was impossible due to seizure.

In the comparative member 2, the surface of the substrate 11 is coated with PTFE resin with an even thickness, and the same annular groove as in this embodiment is provided in the surface. For the comparative member 2, wear resistance was good, but other sliding properties were poor or no effect.

In the comparative member 3, the surface of the substrate 11 is coated with MoS₂ resin with an even thickness. For the comparative member 3, sliding properties other than wear resistance were good but wear resistance was no effect. In the comparative member 4, the surface of the substrate 11 is covered with mixed resin of PTFE resin and MoS₂ resin with an even thickness. For the comparative member 4, sliding properties were generally poor.

As shown in FIG. 4, it is apparent that the swash plate 3 of this embodiment is superior in all the sliding properties.

As described above, the swash plate 3 of this embodiment has the superior sliding properties for the following reasons. Specifically, in the surfaces of the sliding surfaces 3A and 3B of the swash plate 3, the annular groove 14 is generally maintained to match the annular groove 12A in the first resin layer 12, and the minute countless irregularities are formed in the entire surface of the second resin layer 13. Thus, the lubricating oil can be easily held in the sliding surfaces 3A and 3B to form an oil film. Thus, the oil film can be easily formed on the sliding surfaces 3A and 3B, and it is supposed that the swash plate 3 of this embodiment has good oil holding properties.

Also, in the initial stage of sliding in which the sliding surfaces 3A and 3B of the swash plate 3 start sliding with respect to the sliding surfaces 4A and 4B of the shoe 4, the portion of the second resin layer 13 of soft resin at the protrusion 12B wears, and thus the swash plate 3 of this embodiment has a good fit to the sliding surface 4A of the shoe 4.

Further, as shown in FIG. 3, when the second resin layer 13 coating the top of the protrusion 12B wears and the protrusion 12B of the first resin layer 12 is exposed, the protrusion 12B of hard resin slides with respect to the sliding surface 4A of the shoe 4 to prevent wear of the second resin layer 13. Also, it is supposed that the wearing powdery second resin layer 13 adheres to the exposed protrusion 12B to improve wear resistance of the swash plate 3.

Also in the state shown in FIG. 3, there is the second resin layer 13 adjacent to the exposed protrusion 12B of the exposed first resin layer 12, and thus the lubricating oil is held in the second resin layer 13. Thus, it is supposed that the swash plate 3 of this embodiment also has good seizure resistance.

As described above, according to the swash plate 3 and the production method thereof of this embodiment, the swash plate 3 having high wear resistance and seizure resistance can be provided even in a poor lubrication state where the lubricating oil is insufficiently supplied.

Also, according to this embodiment, a swash plate can be provided suitable as a swash plate 3 for a swash plate type compressor used in a severe environment using a new coolant or a CO₂ coolant.

Further, in the conventional swash plate, the relatively expensive intermediate layer such as a metal layer, a plated layer or a chemical conversion coating layer is provided on the surface of the substrate 11, but such an intermediate layer is omitted in this embodiment. Thus, according to this embodiment, one step of the production process of the swash plate 3 can be omitted, which can reduce production costs of the swash plate 3.

Multiple concentric annular grooves may be formed instead of the spiral annular groove 12A provided in the surface of the first resin layer 12. With such a configuration, the same operation and effect as the above-described embodiment can be obtained.

In the embodiment, the iron-based substrate 11 is used, but an aluminum- or copper-based substrate 11 may be used.

REFERENCE SIGNS LIST

-   3 . . . swash plate -   3A, 3B . . . sliding surface -   4 . . . shoe -   11 . . . substrate -   12 . . . first resin layer -   12A . . . annular groove -   13 . . . second resin layer 

1. A swash plate having a sliding surface that slides with respect to a shoe, comprising: a substrate made of any of iron-, aluminum-, or copper-based materials; a hard first resin layer provided to coat a surface of the substrate and having an annular groove formed in an outer side surface; and a soft second resin layer provided to coat the surface of the first resin layer and formed to match a sectional shape of the annular groove in the first resin layer, wherein in an initial stage of sliding with respect to the shoe, the second resin layer is the sliding surface, and when the second resin layer partially wears and a protrusion of the annular groove in the first resin layer is exposed, the protrusion and the second resin layer adjacent to the protrusion are the sliding surface.
 2. The swash plate according to claim 1, wherein a thickness of the protrusion of the annular groove in the first resin layer is larger than a thickness of the second resin layer.
 3. The swash plate according to claim 2, wherein a thickness B of a portion of the second resin layer coating the protrusion of the annular groove in the first resin layer and a thickness A of a portion of the second resin layer coating a recess of the annular groove have a size relationship of 3/2A≧B.
 4. The swash plate according to claim 1, wherein the first resin layer is a thermosetting resin binder to which at least one of graphite, carbon, MoS₂ and PTFE is added, and the second resin layer is a thermosetting resin binder to which at least one of MoS₂ and PTFE is added.
 5. A production method of a swash plate according to claim 1, comprising the steps of: applying a resin paint for a first resin layer composed of hard resin to an end surface of a substrate to provide the first resin layer; drying and/or baking the first resin layer and then forming a minute annular groove in a surface of the first resin layer; applying a resin paint for a second resin layer composed of soft resin to the first resin layer provided with the annular groove; then rotating the substrate at high speeds to remove unnecessary parts of the resin paint for the second resin layer; and forming the second resin layer to match a sectional shape of the surface of the first resin layer. 